SABIC Innovative Plastics Noryl PX4058 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl PX4058 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPO, polyolefin blend. Improved chemical resistance. 253F (125C) HDT.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D 785 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 114 % | 114 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.49 J/cm @Temperature -40.0 °C |
2.79 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 4.80 J/cm @Temperature 23.0 °C |
8.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 2.67 J/cm @Temperature -30.0 °C |
5.00 ft-lb/in @Temperature -22.0 °F |
ASTM D 4812 |
| 19.81 J/cm @Temperature 23.0 °C |
37.11 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 | |
| Impact Test | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| 2.00 J @Temperature -30.0 °C |
1.48 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg |
8.0 @Load 2.20 lb |
CS-17; ASTM D 1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 6.40 mm |
252 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 20 Minutes Milling
- KKPC KOSYN KSL 208 Styrene-Butadiene Latex
- Mitsui Arlenâ„¢ AE4200N Modified Nylon 6T, for Tribolic Applications, Flame Retardant (DAM)
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- Formosa Plastics Formolene® E922 Film HDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Atomite Whiting Filler
- Teknor Apex APEX® 3050-H Polyvinyl Chloride, Flexible
- Parker Chomerics CHO-BOND 580 Conductive Epoxy
- SABIC Innovative Plastics Lexan® FXE1434T PC Copolymer (Europe-Africa-Middle East)
- Materion AlBeMet® AM 162 Extruded Bar, Annealed
Copyright © lookpolymers.com All Rights Reserved