SABIC Innovative Plastics Noryl PX1404 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl PX1404 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. High Heat. FDA compliant with restrictions. Injection Molding and Extrusion.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 20 % | 20 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.70 J/cm @Temperature -40.0 °C |
3.18 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Gardner Impact | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 148 °C @Thickness 6.40 mm |
298 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Fujipoly Industries Sarcon® NR-Hc Gap Filler Pad
- Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes
- LATI Latilub 85-10T G/30 PES, 30% Glass Fiber Reinforced, PTFE Filled
- Struktol STRUKSILON 8023 Silicone Stabilizer for PU-Rigid Foam
- Sumitomo Chemical ESPOLEX® 820 Thermoplastic Elastomer
- SCG Chemicals EL-Leneâ„¢ M3204 Butene (C4) Rotational Molding Resin
- Williams Advanced Alloys WS118 Solder
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 400 Gauge
- 3M Dyneon™ FT 2320 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved