SABIC Innovative Plastics Noryl HIPS3191 PS

Category Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl HIPS3191 PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D 792
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
 0.25 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 2.6 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 2.6 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D 1238
7.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 21.0 MPa
3050 psi
50 mm/min; ISO 527
25.0 MPa
3630 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 30.0 MPa
4350 psi
50 mm/min; ISO 527
32.0 MPa
4640 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 43 %
43 %
Type I, 50 mm/min; ASTM D 638
45.7 %
45.7 %
50 mm/min; ISO 527
Elongation at Yield 1.6 %
1.6 %
50 mm/min; ISO 527
1.7 %
1.7 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.14 GPa
310 ksi
5 mm/min; ASTM D 638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 46.0 MPa
6670 psi
2 mm/min; ISO 178
48.0 MPa
6960 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.24 GPa
325 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.36 J/cm

@Temperature -30.0 °C
 2.55 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
2.70 J/cm

@Temperature 23.0 °C
 5.06 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 20.0 J

@Temperature 23.0 °C
 14.8 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
96.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 53.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 86.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
96.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 53.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
76.0 °C

@Thickness 3.20 mm
 169 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 90.0 °C
194 °F
Rate B/50; ASTM D 1525
90.0 °C
194 °F
Rate B/50; ISO 306
92.0 °C
198 °F
Rate B/120; ISO 306