SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR additives to deliver UL94 V-0 performance at 1.5 mm. Noryl FXN2090H resin is currently available in custom black colors and may be an excellent material candidate for consumer electronics applications requiring high gloss aesthetics, scratch resistance and FR performance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D 792
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.060 %
0.060 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.18 %

@Temperature 23.0 °C
0.18 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D 1238
25 g/10 min

@Load 2.16 kg,
Temperature 280 °C
25 g/10 min

@Load 4.76 lb,
Temperature 536 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
58.0 MPa
8410 psi
50 mm/min; ISO 527
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 6.3 %
6.3 %
50 mm/min; ISO 527
7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 3.6 %
3.6 %
50 mm/min; ISO 527
3.7 %
3.7 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.64 GPa
383 ksi
1 mm/min; ISO 527
2.68 GPa
389 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 99.0 MPa
14400 psi
1.3 mm/min, 50 mm span; ASTM D 790
105 MPa
15200 psi
2 mm/min; ISO 178
Flexural Modulus 2.51 GPa
364 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.66 GPa
386 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.450 J/cm

@Temperature -30.0 °C
0.843 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
1.00 J/cm

@Temperature 23.0 °C
1.87 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 17.0 J

@Temperature 23.0 °C
12.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
84.0 °C

@Thickness 3.20 mm
183 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 107 °C
225 °F
Rate B/50; ISO 306
109 °C
228 °F
Rate B/120; ISO 306
109 °C
228 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
Glow Wire Test 725 °C

@Thickness 2.00 mm
1340 °F

@Thickness 0.0787 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
725 °C

@Thickness 1.00 mm
1340 °F

@Thickness 0.0394 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
750 °C

@Thickness 3.00 mm
1380 °F

@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties Metric English Comments
Gloss 97 %
97 %
untextured, 60 degrees; ASTM D 523
Electrical Properties Metric English Comments
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
PLC code 0; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C pass
IEC 60695-10-2
Copyright © lookpolymers.com All Rights Reserved