SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, strong flame-retardant, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-1 requirement. 80C temperature rating as defined by UL 1581. 85 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | 50 mm/min; ISO 527 |
| 17.0 MPa | 2470 psi | Type I, 50 mm/min; ASTM D638 | |
| 19.0 MPa | 2760 psi | UL 1581 | |
| 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 122 % | 122 % | 50 mm/min; ISO 527 |
| 147 % | 147 % | Type I, 50 mm/min; ASTM D638 | |
| 165 % | 165 % | after 7days @113°C; UL 1581 | |
| 200 % | 200 % | UL 1581 | |
| Flexural Modulus | 0.140 GPa | 20.3 ksi | 12.5 mm/min; ISO 178 |
| 0.150 GPa | 21.8 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 17 % @Load 0.250 kg, Temperature 100 °C |
17 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.50e+15 ohm-cm | 2.50e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 94 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 76 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |
Users viewing this material also viewed the following:
- Polymer Resources TP-HG40 Polybutylene Terephthalate, 40% Glass Reinforced Alloy
- Multibase Multibatch® MP 52631 BOPP White Pearlised Film
- Lushan PA6+30% GF Nylon Toughener/PA Impact Modifier
- Polyram PlusTek PB304G7 Nylon 6, 35% Glass Fiber
- Dow Corning MOLYKOTE® 33 EXTREME LOW TEMPERATURE BEARING GREASE, LIGHT
- ChevronTexaco Concrete Form Oil VOC
- ExxonMobil Mobil Vactra 2
- E-Polymers SEPAZ® V250A 50% Glass Fiber Reinforced PPA
- Henkel Fixodine Z Surface Conditioner
Copyright © lookpolymers.com All Rights Reserved