SABIC Innovative Plastics NORYL WCA875 PPE-TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCA875 PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced tensile elongation, capable of VW-1 performance and 105C temperature rating as defined by UL 1581. 87 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0mm wire with 0.12mm X 20 stranded coppoer conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 250 °C |
16 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 | 87 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| 16.0 MPa | 2320 psi | 50 mm/min; ISO 527 | |
| 26.0 MPa | 3770 psi | after 7days @136°C; UL 1581 | |
| 27.0 MPa | 3920 psi | UL 1581 | |
| Elongation at Break | 170 % | 170 % | 50 mm/min; ISO 527 |
| 180 % | 180 % | Type I, 50 mm/min; ASTM D638 | |
| 190 % | 190 % | after 7days @136°C; UL 1581 | |
| 250 % | 250 % | UL 1581 | |
| Flexural Modulus | 0.0400 GPa | 5.80 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
| 0.0400 GPa | 5.80 ksi | 12.5 mm/min; ISO 178 | |
| Heat Distortion | 10 % @Load 0.250 kg, Temperature 121 °C |
10 % @Load 0.551 lb, Temperature 250 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 105 °C | 221 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 29 % | 29 % | ISO 4589 |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1e+17 ohm-cm | <= 1e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 22.8 kV/mm @Thickness 2.00 mm |
579 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0035 @Frequency 1.00e+6 Hz |
0.0035 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 146 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 112 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |