SABIC Innovative Plastics NORYL WCA105 PPE-TPE

Category Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL WCA105 PPE-TPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requirements as defined by UL 1581. 56 Shore D hardness. Excellent processing using standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 173000 sec
0.10 %

@Time 48.0 hour
ASTM D570
Melt Flow 5.1 g/10 min

@Load 10.0 kg,
Temperature 250 °C
5.1 g/10 min

@Load 22.0 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 56
56
ISO 868
Tensile Strength at Break 23.0 MPa
3340 psi
Type I, 50 mm/min; ASTM D638
23.0 MPa
3340 psi
50 mm/min; ISO 527
33.0 MPa
4790 psi
UL 1581
36.0 MPa
5220 psi
after 7days @136°C; UL 1581
Elongation at Break 85 %
85 %
Type I, 50 mm/min; ASTM D638
90 %
90 %
50 mm/min; ISO 527
156 %
156 %
after 7days @136°C; UL 1581
197 %
197 %
UL 1581
Flexural Modulus 0.650 GPa
94.3 ksi
12.5 mm/min, 100 mm span; ASTM D790
0.720 GPa
104 ksi
12.5 mm/min; ISO 178
Tear Strength 25.0 kN/m
143 pli
ISO 6383
Heat Distortion 26 %

@Load 0.250 kg,
Temperature 121 °C
26 %

@Load 0.551 lb,
Temperature 250 °F
UL 1581
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
UL temperature rating; UL 1581
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C

@Thickness 6.40 mm
185 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 102 °C
216 °F
Rate A/50; ISO 306
Brittleness Temperature <= -40.0 °C
<= -40.0 °F
ASTM D746
Oxygen Index 25 %
25 %
ISO 4589
Glow Wire Test 750 °C
1380 °F
IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 3.90e+16 ohm-cm
3.90e+16 ohm-cm
IEC 60093
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
2.5

@Frequency 1.00e+6 Hz
IEC 60250
2.6

@Frequency 50.0 - 60.0 Hz
2.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 26.0 kV/mm

@Thickness 2.00 mm
660 kV/in

@Thickness 0.0787 in
in oil; IEC 60243-1
Dissipation Factor 0.0038

@Frequency 1.00e+6 Hz
0.0038

@Frequency 1.00e+6 Hz
IEC 60250
0.024

@Frequency 50.0 - 60.0 Hz
0.024

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Smoke Density on 0.5mm plaque, Flame, Ds, max 150
ASTM E 662
Smoke Density on 0.5mm plaque, Non-flame, Ds, max 75
ASTM E 662
VW-1 Pass
UL 1581