SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* V0150B is an unfilled, injection moldable modified polyphenylene ether resin.. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 1.5 mm and a UL94 5Va rating at 2.0 mm. Noryl V0150B is also halogen free according to VDE/DIN 472 part 815 and may be an excellent material candidate where flame resistance and high temperature resistance is required.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.18 %
0.18 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 3.5 g/10 min

@Load 5.00 kg,
Temperature 280 °C
3.5 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 5.00 kg,
Temperature 300 °C
10 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 113 MPa
16400 psi
ISO 2039-1
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 70.0 MPa
10200 psi
Type I, 50 mm/min; ASTM D638
70.0 MPa
10200 psi
50 mm/min; ISO 527
Elongation at Break 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.50 GPa
363 ksi
5 mm/min; ASTM D638
2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D790
110 MPa
16000 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.55 GPa
370 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.30 J/cm
6.18 ft-lb/in
ASTM D256
1.80 J/cm

@Temperature -30.0 °C
3.37 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 35
35
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
90.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 140 °C
<= 284 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
135 °C

@Thickness 3.20 mm
275 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 145 °C
293 °F
Rate B/50; ISO 306
155 °C
311 °F
Rate B/120; ISO 306
155 °C
311 °F
Rate B/50; ASTM D1525
160 °C
320 °F
Rate A/50; ISO 306
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 115 °C
239 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VA

@Thickness 2.00 mm
5VA

@Thickness 0.0787 in
UL 94
Oxygen Index 32 %
32 %
ISO 4589
Glow Wire Test 775 °C
1430 °F
IEC 60695-2-13
775 °C
1430 °F
IEC 60695-2-13
775 °C
1430 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
2.8

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
26.0 kV/mm

@Thickness 1.60 mm
660 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
33.0 kV/mm

@Thickness 0.800 mm
838 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.00090

@Frequency 50.0 - 60.0 Hz
0.00090

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0030

@Frequency 1.00e+6 Hz
0.0030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2