Material Notes:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V1, UL746C F1. Dielectric strength. Suitable for E/E market indoor/outdoor applications.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Water Absorption 0.060 %

@Time 86400 sec
0.060 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Flow 8.5 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.5 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 61.0 MPa
8850 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
20.7 %
20.7 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
4.3 %
4.3 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
50 mm/min; ASTM D638
2.67 GPa
387 ksi
1 mm/min; ISO 527
Flexural Yield Strength 98.0 MPa
14200 psi
2.6 mm/min, 100 mm span; ASTM D790
99.0 MPa
14400 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.56 GPa
371 ksi
2 mm/min; ISO 178
2.70 GPa
392 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.80 J/cm
3.37 ft-lb/in
ASTM D256
1.06 J/cm

@Temperature -30.0 °C
1.99 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 26.0 J/cm
48.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 49.0 J

@Temperature 23.0 °C
36.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 88.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
264 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D648
129 °C

@Thickness 6.40 mm
264 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
112 °C

@Thickness 3.20 mm
234 °F

@Thickness 0.126 in
unannealed; ASTM D648
118 °C

@Thickness 6.40 mm
244 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 132 °C
270 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.47 mm
V-1

@Thickness 0.0579 in
UL 94
V-0

@Thickness 5.99 mm
V-0

@Thickness 0.236 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.30e+16 ohm-cm
2.30e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 2.46

@Frequency 1.00e+6 Hz
2.46

@Frequency 1.00e+6 Hz
ASTM D150
2.52

@Frequency 50.0 - 60.0 Hz
2.52

@Frequency 50.0 - 60.0 Hz
ASTM D150
Dielectric Strength 18.1 kV/mm

@Thickness 3.20 mm
460 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0021

@Frequency 1.00e+6 Hz
0.0021

@Frequency 1.00e+6 Hz
ASTM D150
0.0034

@Frequency 50.0 - 60.0 Hz
0.0034

@Frequency 50.0 - 60.0 Hz
ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Radiant Panel Listing RP100
UL Tested
UV-light, water exposure/immersion F1
UL 746C