SABIC Innovative Plastics NORYL RN1300 PPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL RN1300 PPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass/mineral reinforced PPE. Nonchlorinated, nonbrominated, flame-retardant. Black and gray.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0045 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0045 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 26.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
26.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 102 MPa | 14800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 6.9 % | 6.9 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.89 GPa | 709 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C @Temperature -40.0 - 60.0 °C |
19.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 0.760 mm |
V-1 @Thickness 0.0299 in |
UL 94 |
| V-0 @Thickness 1.52 mm |
V-0 @Thickness 0.0598 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |