SABIC Innovative Plastics NORYL PX2907 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX2907 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+HIPS GF10% FR V-1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15.3 g/10 min @Load 5.00 kg, Temperature 300 °C |
15.3 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | SABIC - Japan Method |
| Elongation at Break | 11 % | 11 % | SABIC - Japan Method |
| Flexural Strength | 122 MPa | 17700 psi | ASTM D790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | ASTM D790 |
| Izod Impact, Notched | 0.920 J/cm | 1.72 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C @Thickness 6.40 mm |
268 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 0.710 mm |
V-1 @Thickness 0.0280 in |
UL 94 |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 |