SABIC Innovative Plastics NORYL PX2391 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX2391 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PX2391 is a 10% glass fiber reinforced, heat stabilized, low odor and low emission NORYL(R) grade for interior automotive applications, especially instrument panels
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Melt Index of Compound | 18 g/10 min @Load 2.16 kg, Temperature 300 °C |
18 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 53 T 25 PP, 25% mineral filling
- Precision Polymer Engineering V70W Fluoroelastomer Compound
- Palm Labs Adhesives TURBO FUSE SERIES 110 MEDICAL DEVICES APPROVED (100 Viscosity) Rapid Bonding Adhesive
- Parker Chomerics CHO-SEAL® 6370 Conductive Elastomer
- Sibur Neva Polyvinyl Chloride (PVC)
- EMS-Grivory Grivory® BG-15 S PA6-GF15
- Covestro Desmopan® 453 Urethane Thermoplastic Elastomer (discontinued **)
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE
- Buckeye Polymers BP RPP 1509 GK BLK Polypropylene, 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved