Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX2060 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and V0@ 2.5mm with a specific density of 1.1 g/cm^3. Noryl PX2060 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.13 %
0.13 %
ISO 62
Viscosity 66000 cP
66000 cP
Melt Viscosity, 280°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 42 g/10 min

@Load 3.80 kg,
Temperature 200 °C
42 g/10 min

@Load 8.38 lb,
Temperature 392 °F
ASTM D1238
61 g/10 min

@Load 5.00 kg,
Temperature 250 °C
61 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
Melt Index of Compound 20 g/10 min

@Load 1.20 kg,
Temperature 280 °C
20 g/10 min

@Load 2.65 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
41 g/10 min

@Load 2.16 kg,
Temperature 280 °C
41 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break 11 %
11 %
50 mm/min; ISO 527
12 %
12 %
Type I, 50 mm/min; ASTM D638
12 %
12 %
Nominal Strain, 5 mm/min; ASTM D638
Elongation at Yield 2.9 %
2.9 %
50 mm/min; ISO 527
3.0 %
3.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
50 mm/min; ASTM D638
2.42 GPa
351 ksi
1 mm/min; ISO 527
Flexural Yield Strength 82.0 MPa
11900 psi
2 mm/min; ISO 178
84.0 MPa
12200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.53 GPa
367 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.780 J/cm
1.46 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*4; ISO 180/1U
53.0 kJ/m²

@Temperature -30.0 °C
25.2 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C

@Thickness 3.20 mm
176 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 91.0 °C
196 °F
Rate B/50; ISO 306
93.0 °C
199 °F
Rate B/120; ISO 306
105 °C
221 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94 by SABIC-IP
V-0

@Thickness 2.50 mm
V-0

@Thickness 0.0984 in
UL 94 by SABIC-IP
Oxygen Index 28 %
28 %
ISO 4589
Glow Wire Test 700 °C
1290 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 2.60e+16 - 3.60e+16 ohm-cm
2.60e+16 - 3.60e+16 ohm-cm
ASTM D257
2.60e+16 - 3.60e+16 ohm-cm
2.60e+16 - 3.60e+16 ohm-cm
IEC 60093
Surface Resistance 3.40e+15 - 4.50e+15 ohm
3.40e+15 - 4.50e+15 ohm
ASTM D257
3.40e+15 - 4.50e+15 ohm
3.40e+15 - 4.50e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.6

@Frequency 1.00e+6 Hz
2.6

@Frequency 1.00e+6 Hz
IEC 60250
2.69

@Frequency 1.00e+6 Hz
2.69

@Frequency 1.00e+6 Hz
ASTM D150
Dissipation Factor 0.0023

@Frequency 1.00e+6 Hz
0.0023

@Frequency 1.00e+6 Hz
ASTM D150
0.0023

@Frequency 1.00e+6 Hz
0.0023

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
225 V
225 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746A