Material Notes:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Flow 37 g/10 min

@Load 5.00 kg,
Temperature 280 °C
37 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 37 g/10 min

@Load 5.00 kg,
Temperature 280 °C
37 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.0 MPa
5950 psi
Type I, 50 mm/min; ASTM D638
43.0 MPa
6240 psi
50 mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 12.5 %
12.5 %
50 mm/min; ISO 527
17 %
17 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 2.8 %
2.8 %
50 mm/min; ISO 527
3.1 %
3.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
50 mm/min; ASTM D638
2.46 GPa
357 ksi
1 mm/min; ISO 527
Flexural Yield Strength 76.0 MPa
11000 psi
2 mm/min; ISO 178
79.0 MPa
11500 psi
2.6 mm/min, 100 mm span; ASTM D790
80.0 MPa
11600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.43 GPa
352 ksi
ASTM D790
2.48 GPa
360 ksi
2 mm/min; ISO 178
Izod Impact, Notched 3.00 J/cm
5.62 ft-lb/in
ASTM D256
0.900 J/cm

@Temperature -30.0 °C
1.69 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 11.74 J/cm
21.99 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 22.0 kJ/m²
10.5 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.30 J/cm²
10.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 89.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
49.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 103 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
84.0 °C

@Thickness 3.20 mm
183 °F

@Thickness 0.126 in
unannealed; ASTM D648
88.0 °C

@Thickness 6.40 mm
190 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
72.0 °C

@Thickness 3.20 mm
162 °F

@Thickness 0.126 in
unannealed; ASTM D648
78.0 °C

@Thickness 6.40 mm
172 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 94.0 °C
201 °F
Rate B/50; ISO 306
97.0 °C
207 °F
Rate B/120; ISO 306
107 °C
225 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 95.0 °C
203 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 95.0 °C
203 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.01 mm
HB

@Thickness 0.0398 in
UL 94
V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
UL 94
5VA

@Thickness 2.99 mm
5VA

@Thickness 0.118 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 3.30e+16 ohm-cm
3.30e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ASTM D257
Dielectric Constant 2.53

@Frequency 1.00e+6 Hz
2.53

@Frequency 1.00e+6 Hz
ASTM D150
2.67

@Frequency 50.0 - 60.0 Hz
2.67

@Frequency 50.0 - 60.0 Hz
ASTM D150
Dielectric Strength 17.7 kV/mm

@Thickness 3.20 mm
450 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0026

@Frequency 1.00e+6 Hz
0.0026

@Frequency 1.00e+6 Hz
ASTM D150
0.012

@Frequency 50.0 - 60.0 Hz
0.012

@Frequency 50.0 - 60.0 Hz
ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
UV-light, water exposure/immersion F1
UL 746C