SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl PPX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High modulus/impact/heat PPE+PP
Physical Properties Metric English Comments
Specific Gravity 0.990 g/cc
0.990 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 14 g/10 min

@Load 5.00 kg,
Temperature 260 °C
14 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 35.0 MPa
5080 psi
Type I, 50 mm/min; ASTM D638
35.0 MPa
5080 psi
50 mm/min; ISO 527
Elongation at Break 75 %
75 %
50 mm/min; ISO 527
125 %
125 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 8.0 %
8.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.24 GPa
180 ksi
50 mm/min; ASTM D638
1.37 GPa
199 ksi
1 mm/min; ISO 527
Flexural Yield Strength 51.0 MPa
7400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.37 GPa
199 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
ASTM D256
Dart Drop, Total Energy 30.0 J

@Temperature -30.0 °C
22.1 ft-lb

@Temperature -22.0 °F
ASTM D3763
37.0 J

@Temperature 23.0 °C
27.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 162 µm/m-°C

@Temperature -40.0 - 40.0 °C
90.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 97.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
54.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 112 °C

@Thickness 3.20 mm
234 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 86.0 °C
187 °F
Rate B/50; ASTM D1525
131 °C
268 °F
Rate A/50; ISO 306