SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0023 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0023 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0025 - 0.0076 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0076 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 260 °C |
2.6 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 7.7 % | 7.7 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 129 MPa | 18700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.55 GPa | 805 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.65 J/cm | 3.09 ft-lb/in | ASTM D256 |
| 1.01 J/cm @Temperature -30.0 °C |
1.89 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 8.27 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 19.0 J @Temperature 23.0 °C |
14.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 20.0 J @Temperature -30.0 °C |
14.8 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 162 °C | 324 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Polygon Polylube™ Fiber Series Epoxy Composite Bearings
- GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade
- Ineos ABS Lustran® ABS 240 Injection Molding Grade
- Solvay Specialty Polymers Algoflon® F 5/S Polytetrafluoroethylene (PTFE)
- Solvay Specialty Polymers AvaSpire® AV-621 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
- SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK
- SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- ExxonMobil Mobil Pegasus 1 40
- Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved