SABIC Innovative Plastics NORYL NWP100 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NWP100 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPO/HIPS Unfilled high impact extrusion grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC Method |
| Melt Flow | 8.5 g/10 min @Load 10.0 kg, Temperature 250 °C |
8.5 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 10 mm/min; SABIC - Japan Method |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 10 mm/min; SABIC - Japan Method |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.05 GPa | 297 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 3.43 J/cm | 6.43 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |