SABIC Innovative Plastics NORYL NH5120C PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL NH5120C PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* NH5120C resin is a modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, good chemical resistance, and low specifc gravity for light weight parts. The resin will be available in custom colors and is suitable for injection molding.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %
0.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 20.6 g/10 min

@Load 5.00 kg,
Temperature 300 °C
20.6 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 21 g/10 min

@Load 5.00 kg,
Temperature 300 °C
21 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Tensile Strength, Yield 64.0 MPa
9280 psi
50 mm/min; ISO 527
68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 12.5 %
12.5 %
50 mm/min; ISO 527
13 %
13 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.3 %
4.3 %
50 mm/min; ISO 527
4.5 %
4.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.52 GPa
365 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 101 MPa
14600 psi
1.3 mm/min, 50 mm span; ASTM D790
103 MPa
14900 psi
2 mm/min; ISO 178
Flexural Modulus 2.58 GPa
374 ksi
2 mm/min; ISO 178
2.65 GPa
384 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.28 J/cm
4.27 ft-lb/in
ASTM D256
1.45 J/cm

@Temperature -30.0 °C
2.72 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 7.50 µm/m-°C

@Temperature -40.0 - 40.0 °C
4.17 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
75.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 137 °C
279 °F
Rate B/50; ASTM D1525
137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94 by SABIC-IP