SABIC Innovative Plastics NORYL N190X PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL N190X PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. Dielectric strength. Suitable for E/E market applications.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Water Absorption 0.080 %

@Time 86400 sec
0.080 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 19.3 g/10 min

@Load 10.0 kg,
Temperature 250 °C
19.3 g/10 min

@Load 22.0 lb,
Temperature 482 °F
ASTM D1238
Melt Index of Compound 23 g/10 min

@Load 5.00 kg,
Temperature 280 °C
23 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength at Break 47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
50 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 9.0 %
9.0 %
Type I, 50 mm/min; ASTM D638
9.2 %
9.2 %
50 mm/min; ISO 527
Elongation at Yield 3.2 %
3.2 %
50 mm/min; ISO 527
3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.58 GPa
374 ksi
50 mm/min; ASTM D638
2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 87.0 MPa
12600 psi
2 mm/min; ISO 178
91.0 MPa
13200 psi
2.6 mm/min, 100 mm span; ASTM D790
98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.35 GPa
341 ksi
2 mm/min; ISO 178
2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.45 J/cm
4.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.20 J/cm
13.5 ft-lb/in
ASTM D4812
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/2C
Dart Drop, Total Energy 50.0 J
36.9 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Taber Abrasion, mg/1000 Cycles 76
76
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C
180 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
78.0 °C

@Thickness 3.20 mm
172 °F

@Thickness 0.126 in
unannealed; ASTM D648
86.0 °C

@Thickness 6.40 mm
187 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 104 °C
219 °F
Rate B/50; ASTM D1525
107 °C
225 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Oxygen Index 39 %
39 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.80e+16 ohm-cm
1.80e+16 ohm-cm
ASTM D257
Dielectric Constant 2.6

@Frequency 100000 Hz
2.6

@Frequency 100000 Hz
ASTM D150
2.74

@Frequency 100 Hz
2.74

@Frequency 100 Hz
ASTM D150
Dielectric Strength 19.2 kV/mm

@Thickness 3.20 mm
488 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0055

@Frequency 100000 Hz
0.0055

@Frequency 100000 Hz
ASTM D150
0.013

@Frequency 100 Hz
0.013

@Frequency 100 Hz
ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A