SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in custom colors. Noryl HNA033 resin may be an excellent material candidate for applications requiring multiple sterilization cycles. Noryl HNA033 resin is biocompatible per ISO 10993 (color dependent).
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.15 %
0.15 %
ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0070 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.3 g/10 min

@Load 5.00 kg,
Temperature 300 °C
8.3 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 68.0 MPa
9860 psi
50 mm/min; ISO 527
71.0 MPa
10300 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 14.8 %
14.8 %
50 mm/min; ISO 527
30 %
30 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.2 %
5.2 %
50 mm/min; ISO 527
5.3 %
5.3 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.31 GPa
335 ksi
5 mm/min; ASTM D638
2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
107 MPa
15500 psi
2 mm/min; ISO 178
Flexural Modulus 2.46 GPa
357 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.59 GPa
376 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.92 J/cm
3.60 ft-lb/in
ASTM D256
1.44 J/cm

@Temperature -30.0 °C
2.70 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 47.0 J

@Temperature 23.0 °C
34.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 68.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
68.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 160 °C
320 °F
Rate B/50; ISO 306
161 °C
322 °F
Rate B/50; ASTM D1525
162 °C
324 °F
Rate B/120; ISO 306