SABIC Innovative Plastics NORYL GTX GTX986 PPE+PA66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX986 PPE+PA66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Conductive GTX, CTE 6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.800 % | 0.800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.0 % | 3.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 280 °C |
13 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | Type I, 50 mm/min; ASTM D638 |
| 15 % | 15 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 3.10 GPa | 450 ksi | 50 mm/min; ASTM D638 |
| 3.70 GPa | 537 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 100 MPa | 14500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.70 GPa | 537 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/50; ISO 306 |
| 202 °C | 396 °F | Rate B/50; ASTM D1525 | |
| 205 °C | 401 °F | Rate B/120; ISO 306 |