- HOME
- POLYMER SEARCH
- Thermoplastic
- Polystyrene (PS)
- SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA
SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX964W resin is a blend of Polyphenylene Ether and Polyamide resin with very high impact and high flow. The material wsa designed for large parts, body panels, and thinwall applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 1.19 % | 1.19 % | 50% RH; ASTM D570 |
| 3.5 % | 3.5 % | ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | SABIC Method |
| Melt Index of Compound | 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
| 56 % | 56 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| 73.0 MPa | 10600 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| 1.83 GPa | 265 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.28 J/cm | 9.89 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 41.0 J @Temperature 23.0 °C |
30.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 185 °C @Thickness 6.40 mm |
365 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ISO 306 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| 240 °C | 464 °F | Rate A/50; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Therma-Tech™ SF-6000 TC Polyphenylene Sulfide (PPS) (discontinued **)
- Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Lubrizol Advanced Materials Pearlstick® 48-60/15 Linear Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics ULTEM 2212R PEI (Asia Pacific)
- A. Schulman POLYBATCH™ White LL8425 AP Concentrate Based In LLDPE
- A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy
- DuPont Performance Polymers Zytel® 7331J NC010 Nylon 6 (Unverified Data**)
- SABIC Innovative Plastics LNP THERMOCOMP JF004P PES
- LyondellBasell Hifax™ CB235 Thermoplastic Olefin Resin
Copyright © lookpolymers.com All Rights Reserved