SABIC Innovative Plastics NORYL GTX GTX6203 PPE+PA (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX6203 PPE+PA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption 1.10 %
1.10 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 3.2 %
3.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 280 °C
20 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 20 g/10 min

@Load 5.00 kg,
Temperature 280 °C
20 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
10 %
10 %
5 mm/min; ISO 527
10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.60 GPa
667 ksi
5 mm/min; ASTM D638
4.90 GPa
711 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.80 GPa
551 ksi
1.3 mm/min, 50 mm span; ASTM D790
4.00 GPa
580 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.500 J/cm

@Temperature -30.0 °C
0.937 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1U
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
7.38 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
90.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
190 °C

@Thickness 3.20 mm
374 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 185 °C
365 °F
Rate B/50; ASTM D1525
190 °C
374 °F
Rate B/50; ISO 306
190 °C
374 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2