SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color dependent.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 10.0 kg,
Temperature 280 °C
13 g/10 min

@Load 22.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.0 MPa
13500 psi
Type I, 5 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 93.0 MPa
13500 psi
Type I, 5 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 6.20 GPa
899 ksi
5 mm/min; ASTM D638
6.40 GPa
928 ksi
1 mm/min; ISO 527
Flexural Yield Strength 140 MPa
20300 psi
1.3 mm/min, 50 mm span; ASTM D790
145 MPa
21000 psi
2 mm/min; ISO 178
Flexural Modulus 5.30 GPa
769 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.30 GPa
769 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.830 J/cm
1.55 ft-lb/in
ASTM D256
0.710 J/cm

@Temperature -30.0 °C
1.33 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 4.90 J/cm
9.18 ft-lb/in
ASTM D4812
4.90 J/cm

@Temperature -30.0 °C
9.18 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Dart Drop, Total Energy 16.0 J

@Temperature 23.0 °C
11.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ASTM D1525
140 °C
284 °F
Rate B/50; ISO 306
145 °C
293 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Oxygen Index 26 %
26 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.00080

@Frequency 50.0 - 60.0 Hz
0.00080

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0030

@Frequency 1.00e+6 Hz
0.0030

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2