SABIC Innovative Plastics NORYL FXN121BK PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL FXN121BK PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* FXN121BK is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this resin uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating. FXN121BK is available in black only.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ISO 2039-2
Hardness, H358/30 105 MPa
15200 psi
ISO 2039-1
Tensile Strength at Break 52.0 MPa
7540 psi
50 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 30 %
30 %
Type I, 50 mm/min; ASTM D638
30 %
30 %
50 mm/min; ISO 527
Elongation at Yield 4.6 %
4.6 %
50 mm/min; ISO 527
4.8 %
4.8 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
5 mm/min; ASTM D638
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
0.700 J/cm

@Temperature -30.0 °C
1.31 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 41.0 J

@Temperature 23.0 °C
30.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 60
60
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 118 °C
244 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/50; ASTM D1525
142 °C
288 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
UL 94
Oxygen Index 30 %
30 %
ISO 4589
Glow Wire Test 700 °C
1290 °F
IEC 60695-2-13
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Optical Properties Metric English Comments
Gloss 20 %
20 %
untextured, 60 degrees; ASTM D523
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.7

@Frequency 50.0 - 60.0 Hz
2.7

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.00040

@Frequency 50.0 - 60.0 Hz
0.00040

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2