SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Noryl
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Noryl*FR9310 is a polyphenylene ether resin concentrate with nonhalogenated Flame retardant with Vicat of 165 deg C. Intended for use as an additive or a building block in a variety of thermoplastics and thermoplastic elastomer like polystyrene to improve properties like heat resistance or flame retardance.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ISO 1183
Melt Index of Compound	30 g/10 min @Load 5.00 kg, Temperature 300 °C	30 g/10 min @Load 11.0 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
Tensile Strength, Yield	85.0 MPa	12300 psi	50 mm/min; ISO 527
Elongation at Break	15 %	15 %	50 mm/min; ISO 527
Elongation at Yield	5.0 %	5.0 %	50 mm/min; ISO 527
Tensile Modulus	2.50 GPa	363 ksi	1 mm/min; ISO 527
Flexural Yield Strength	125 MPa	18100 psi	2 mm/min; ISO 178
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	3.00 kJ/m²	1.43 ft-lb/in²	80104; ISO 180/1A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	156 °C	313 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	141 °C	286 °F	Flatw 80104 sp=64mm; ISO 75/Af
Vicat Softening Point	165 °C	329 °F	Rate B/50; ISO 306
	165 °C	329 °F	Rate B/120; ISO 306