SABIC Innovative Plastics NORYL FE1630PW PPE+PS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Noryl
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL FE1630PW PPE+PS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Noryl* FE1630PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid engineering applications. Noryl* FE1630PW has been certified for potable water applications up to 85C in Europe and North America in limited colours

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/in³	ISO 1183
Moisture Absorption	0.0600 %	0.0600 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.20 %	0.20 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.20 mm	0.0010 - 0.0030 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0020 - 0.0050 cm/cm @Thickness 3.20 mm	0.0020 - 0.0050 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	9.0 g/10 min @Load 5.00 kg, Temperature 300 °C	9.0 g/10 min @Load 11.0 lb, Temperature 572 °F	ASTM D1238
Melt Index of Compound	30 g/10 min @Load 10.0 kg, Temperature 300 °C	30 g/10 min @Load 22.0 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	133 MPa	19300 psi	5 mm/min; ISO 527
	134 MPa	19400 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.4 %	2.4 %	Type I, 5 mm/min; ASTM D638
	2.5 %	2.5 %	5 mm/min; ISO 527
Tensile Modulus	9.57 GPa	1390 ksi	5 mm/min; ASTM D638
	9.60 GPa	1390 ksi	1 mm/min; ISO 527
Flexural Strength	192 MPa	27800 psi	2 mm/min; ISO 178
Flexural Modulus	7.76 GPa	1130 ksi	1.3 mm/min, 50 mm span; ASTM D790
	8.12 GPa	1180 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.850 J/cm	1.59 ft-lb/in	ASTM D256
	0.750 J/cm @Temperature -30.0 °C	1.41 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Unnotched	5.05 J/cm	9.46 ft-lb/in	ASTM D4812
	4.65 J/cm @Temperature -30.0 °C	8.71 ft-lb/in @Temperature -22.0 °F	ASTM D4812
Izod Impact, Notched (ISO)	8.00 kJ/m²	3.81 ft-lb/in²	80104; ISO 180/1A
	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	30.0 kJ/m²	14.3 ft-lb/in²	80104; ISO 180/1U
	30.0 kJ/m² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1U
Charpy Impact Unnotched	3.00 J/cm²	14.3 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eU
	3.00 J/cm² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F	Edgew 80104 sp=62mm; ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C @Temperature -40.0 - 40.0 °C	13.9 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	30.0 µm/m-°C @Temperature -40.0 - 40.0 °C	16.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	70.0 µm/m-°C @Temperature -40.0 - 40.0 °C	38.9 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	145 °C	293 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	145 °C @Thickness 3.20 mm	293 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	154 °C	309 °F	Rate B/50; ISO 306
	158 °C	316 °F	Rate B/120; ISO 306
	165 °C	329 °F	Rate A/50; ISO 306