SABIC Innovative Plastics NORYL EM6100 PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL EM6100 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. Unfilled. Good balance of flow/heat/impact. Dimensional stability. Paint adhesion. Suitable for the automotive interior market: HVAC housings, radio components. MS-DB424, WSB-M4D844-A9, GMP.PPE.007.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Water Absorption 0.20 %

@Time 86400 sec
 0.20 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D638
40.0 MPa
5800 psi
ISO 527
Tensile Strength, Yield 42.0 MPa
6090 psi
ISO 527
43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
ISO 527
65 %
65 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 2.8 %
2.8 %
ISO 527
3.0 %
3.0 %
ASTM D638
Tensile Modulus 1.90 GPa
276 ksi
5 mm/min; ASTM D638
2.05 GPa
297 ksi
1 mm/min; ISO 527
Flexural Strength 65.0 MPa
9430 psi
ISO 178
Flexural Yield Strength 66.0 MPa
9570 psi
2.6 mm/min, 100 mm span; ASTM D790
67.0 MPa
9720 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
2.6 mm/min, 100 mm span; ASTM D790
2.10 GPa
305 ksi
ISO 178
2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 4.53 J/cm
8.49 ft-lb/in
ASTM D256
2.50 J/cm

@Temperature -30.0 °C
 4.68 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 3.30 J/cm²
15.7 ft-lb/in²
ISO 179/2C
1.90 J/cm²

@Temperature -30.0 °C
 9.04 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 36.0 J
26.6 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
24.0 J

@Temperature -30.0 °C
 17.7 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D3763
42.0 J

@Temperature 23.0 °C
 31.0 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 117 µm/m-°C

@Temperature 0.000 - 100 °C
 65.0 µin/in-°F

@Temperature 32.0 - 212 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
124 °C

@Thickness 3.20 mm
 255 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
106 °C

@Thickness 3.20 mm
 223 °F

@Thickness 0.126 in
 unannealed; ASTM D648
115 °C

@Thickness 6.40 mm
 239 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 119 °C
246 °F
Rate B/50; ISO 306
123 °C
253 °F
Rate B/120; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.49 mm
 HB

@Thickness 0.0587 in
 UL 94