SABIC Innovative Plastics Lexan® SLX2432D PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® SLX2432D PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.17 %
0.17 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
0.25 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0078 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0078 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
50 mm/min; ISO 527
67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D 638
67.0 MPa
9720 psi
50 mm/min; ISO 527
Elongation at Break 69.9 %
69.9 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.7 %
5.7 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.66 GPa
386 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 100 MPa
14500 psi
2 mm/min; ISO 178
109 MPa
15800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.39 GPa
347 ksi
2 mm/min; ISO 178
2.53 GPa
367 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.660 J/cm

@Temperature -30.0 °C
1.24 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
1.14 J/cm

@Temperature 23.0 °C
2.14 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
25.0 kJ/m²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 78.0 J

@Temperature 23.0 °C
57.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
82.0 J

@Temperature -40.0 °C
60.5 ft-lb

@Temperature -40.0 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 129 °C

@Thickness 3.20 mm
264 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 134 °C
273 °F
Rate B/50; ASTM D 1525
134 °C
273 °F
Rate B/50; ISO 306
136 °C
277 °F
Rate B/120; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
UL 94
Descriptive Properties Value Comments
UV-light, water exposure/immersion F1
UL 746C