SABIC Innovative Plastics Lexan® OQ1022 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® OQ1022 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard Flow OQ Resin
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11 g/10 min

@Load 1.20 kg,
Temperature 250 °C
11 g/10 min

@Load 2.65 lb,
Temperature 482 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 1.20 kg,
Temperature 250 °C
10 g/10 min

@Load 2.65 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Tensile Strength, Yield 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
Type I, 50 mm/min; ASTM D638
108 %
108 %
50 mm/min; ISO 527
Elongation at Yield 5.9 %
5.9 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.42 GPa
351 ksi
50 mm/min; ASTM D638
2.44 GPa
354 ksi
1 mm/min; ISO 527
Flexural Strength 93.0 MPa
13500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.46 GPa
357 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.50 J/cm
10.3 ft-lb/in
ASTM D256
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*3; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 46.0 J

@Temperature 23.0 °C
33.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ASTM D1525
140 °C
284 °F
Rate B/50; ISO 306
141 °C
286 °F
Rate B/120; ISO 306