SABIC Innovative Plastics Lexan® ML6031 PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML6031 PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
0.35 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 76.0 MPa
11000 psi
Type I, 50 mm/min; ASTM D 638
76.0 MPa
11000 psi
50 mm/min; ISO 527
Tensile Strength, Yield 67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D 638
67.0 MPa
9720 psi
50 mm/min; ISO 527
Elongation at Break >= 100 %
>= 100 %
Type I, 50 mm/min; ASTM D 638
>= 100 %
>= 100 %
50 mm/min; ISO 527
Elongation at Yield 6.3 %
6.3 %
Type I, 50 mm/min; ASTM D 638
6.3 %
6.3 %
50 mm/min; ISO 527
Tensile Modulus 2.34 GPa
339 ksi
5 mm/min; ASTM D 638
2.34 GPa
339 ksi
1 mm/min; ISO 527
Flexural Yield Strength 96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D 790
96.0 MPa
13900 psi
2 mm/min; ISO 178
Flexural Modulus 2.12 GPa
307 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.12 GPa
307 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.40 J/cm

@Temperature -30.0 °C
2.62 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
8.20 J/cm

@Temperature 23.0 °C
15.4 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.70 J/cm²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 85.0 J

@Temperature 23.0 °C
62.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
134 °C

@Thickness 3.20 mm
273 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 135 °C
275 °F
Rate B/50; ASTM D 1525
137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Haze 0.50 %

@Thickness 2.54 mm
0.50 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 89 %

@Thickness 2.54 mm
89 %

@Thickness 0.100 in
ASTM D 1003