SABIC Innovative Plastics Lexan® ML6018R PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® ML6018R PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ML6018R is a low viscosity grade exhibiting a high impact performance over standard PC. It contains an enhanced release-agent. Opaque colours only.This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D 792

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	57.0 MPa	8270 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	57.0 MPa	8270 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	103 %	103 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	1.58 GPa	229 ksi	50 mm/min; ASTM D 638
Flexural Yield Strength	75.0 MPa	10900 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	1.83 GPa	265 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	4.80 J/cm @Temperature -30.0 °C	8.99 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	5.66 J/cm @Temperature 23.0 °C	10.6 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Impact Test	70.0 J @Temperature 23.0 °C	51.6 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	115 °C @Thickness 6.40 mm	239 °F @Thickness 0.252 in	unannealed; ASTM D 648