SABIC Innovative Plastics Lexan® ML4588 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML4588 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Extrusion and extrusion blowmolding grade for aircraft applications. Meets FAR 25.853 (60 seconds/30 mils).This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Melt Flow 2.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 65 %
65 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.48 GPa
360 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 7.20 J/cm

@Temperature 23.0 °C
13.5 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Impact Test 59.0 J

@Temperature 23.0 °C
43.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 132 °C

@Thickness 6.40 mm
270 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Descriptive Properties Value Comments
FAA Flammability, FAR 25.853 A/B (A), 1, (I)
FAR 25.853