SABIC Innovative Plastics Lexan® LUX2289 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® LUX2289 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* LUX2289 resin is an injection molding grade with high light reflectance and UV stabilized
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 17 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Elongation at Break 120 %
120 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Yield Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
2.67 GPa
387 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.48 J/cm
12.1 ft-lb/in
ASTM D256
1.65 J/cm

@Temperature -30.0 °C
 3.09 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 1.70 J/cm
3.18 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 52.0 kJ/m²
24.7 ft-lb/in²
80*10*3; ISO 180/1A
13.0 kJ/m²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 170 kJ/m²
80.9 ft-lb/in²
80*10*4; ISO 180/1U
160 kJ/m²

@Temperature -30.0 °C
 76.1 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched 14.0 J/cm²
66.6 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eU
14.0 J/cm²

@Temperature -30.0 °C
 66.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 17.5 J/cm²
83.3 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
17.5 J/cm²

@Temperature -30.0 °C
 83.3 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 69.0 J

@Temperature 23.0 °C
 50.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 136 °C

@Thickness 3.20 mm
 277 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
Annealed 120°C, 2hrs; ISO 75/Ae
124 °C

@Thickness 3.20 mm
 255 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 142 °C
288 °F
Rate B/50; ASTM D1525
144 °C
291 °F
Rate A/50; ISO 306
145 °C
293 °F
Rate B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.00 mm
 HB

@Thickness 0.0394 in
 UL 94
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 UL 94
Glow Wire Test 850 °C
1560 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12