SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO sterilizable.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.060 %
0.060 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %

@Temperature 23.0 °C
0.23 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 23 g/10 min

@Load 1.20 kg,
Temperature 300 °C
23 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
25 g/10 min

@Load 1.20 kg,
Temperature 300 °C
25 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D 638
64.0 MPa
9280 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 122 %
122 %
50 mm/min; ISO 527
129 %
129 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.7 %
5.7 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.31 GPa
335 ksi
50 mm/min; ASTM D 638
2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
99.0 MPa
14400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.15 GPa
312 ksi
2 mm/min; ISO 178
2.38 GPa
345 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.37 J/cm

@Temperature -30.0 °C
4.44 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
7.62 J/cm

@Temperature 23.0 °C
14.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 20.0 kJ/m²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
70.0 kJ/m²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 79.0 J

@Temperature 23.0 °C
58.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
43.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ASTM D 1525
140 °C
284 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Haze 4.5 %

@Thickness 2.54 mm
4.5 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 77 %

@Thickness 2.54 mm
77 %

@Thickness 0.100 in
ASTM D 1003
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2