SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 MFR LEXAN High Flow Ductile Copolymer
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 40 g/10 min

@Load 1.20 kg,
Temperature 300 °C
40 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 250 °C
7.0 g/10 min

@Load 2.65 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
38 g/10 min

@Load 1.20 kg,
Temperature 300 °C
38 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 56.0 MPa
8120 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 97 %
97 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.5 %
5.5 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.18 GPa
316 ksi
1 mm/min; ISO 527
2.27 GPa
329 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.18 GPa
316 ksi
2 mm/min; ISO 178
2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 7.28 J/cm
13.6 ft-lb/in
ASTM D256
1.10 J/cm

@Temperature -30.0 °C
2.06 ft-lb/in

@Temperature -22.0 °F
ASTM D256
6.99 J/cm

@Temperature 0.000 °C
13.1 ft-lb/in

@Temperature 32.0 °F
ASTM D256
Izod Impact, Notched (ISO) 58.0 kJ/m²
27.6 ft-lb/in²
80*10*3; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 6.40 J/cm²
30.5 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 56.0 J

@Temperature 23.0 °C
41.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 95.0 J
70.1 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 129 °C
264 °F
Rate B/50; ISO 306
130 °C
266 °F
Rate B/120; ISO 306
135 °C
275 °F
Rate B/50; ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.582
1.582
ASTM D542
Haze <= 1.0 %

@Thickness 2.54 mm
<= 1.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASS
IEC 60695-10-2