SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.090 %
0.090 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %

@Temperature 23.0 °C
0.12 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on tensile bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 105 %
105 %
50 mm/min; ISO 527
110 %
110 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.6 %
5.6 %
50 mm/min; ISO 527
5.9 %
5.9 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.26 GPa
328 ksi
50 mm/min; ASTM D 638
2.32 GPa
336 ksi
1 mm/min; ISO 527
Flexural Yield Strength 86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D 790
89.0 MPa
12900 psi
2 mm/min; ISO 178
Flexural Modulus 2.17 GPa
315 ksi
2 mm/min; ISO 178
2.27 GPa
329 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.46 J/cm

@Temperature -30.0 °C
4.61 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
6.10 J/cm

@Temperature 23.0 °C
11.4 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Impact Test 61.0 J

@Temperature 23.0 °C
45.0 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.5 µm/m-°C

@Temperature -40.0 - 95.0 °C
39.7 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
71.5 µm/m-°C

@Temperature 23.0 - 80.0 °C
39.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 79.3 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.1 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
79.3 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
122 °C

@Thickness 3.20 mm
252 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 141 °C
286 °F
Rate B/50; ASTM D 1525
141 °C
286 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2