SABIC Innovative Plastics Lexan® FXD9810 PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXD9810 PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-chlorinated, non-brominated Flame retardant PC-siloxane copolymer blend. Excellent processability, super high flow, good impact, UL rated V-0. Limited translucent colors.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.26 %
0.26 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 30 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 30 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 29 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 29 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Elongation at Break 95 %
95 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.6 %
5.6 %
Type I, 50 mm/min; ASTM D638
5.6 %
5.6 %
50 mm/min; ISO 527
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
2.20 GPa
319 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.25 GPa
326 ksi
2 mm/min; ISO 178
Izod Impact, Notched 6.90 J/cm
12.9 ft-lb/in
ASTM D256
2.20 J/cm

@Temperature -30.0 °C
 4.12 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80*10*4; ISO 180/1A
19.0 kJ/m²

@Temperature -30.0 °C
 9.04 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 4.90 J/cm²
23.3 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 63.0 J

@Temperature 23.0 °C
 46.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 38.3 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
70.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 37.8 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
70.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 118 °C

@Thickness 3.20 mm
 244 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 136 °C
277 °F
Rate B/50; ASTM D1525
137 °C
279 °F
Rate B/50; ISO 306
138 °C
280 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 UL 94
V-0

@Thickness 1.20 mm
 V-0

@Thickness 0.0472 in
 UL 94
Glow Wire Test 875 °C
1610 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2