SABIC Innovative Plastics Lexan® FST9705 PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FST9705 PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.110 %
0.110 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.28 %
0.28 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 4.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
4.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
16 g/10 min

@Load 5.00 kg,
Temperature 300 °C
16 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 73.0 MPa
10600 psi
Type I, 50 mm/min; ASTM D638
76.0 MPa
11000 psi
50 mm/min; ISO 527
Tensile Strength, Yield 72.0 MPa
10400 psi
Type I, 50 mm/min; ASTM D638
74.0 MPa
10700 psi
50 mm/min; ISO 527
Elongation at Break 102 %
102 %
Type I, 50 mm/min; ASTM D638
109 %
109 %
50 mm/min; ISO 527
Elongation at Yield 6.7 %
6.7 %
Type I, 50 mm/min; ASTM D638
6.8 %
6.8 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
2.61 GPa
379 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 107 MPa
15500 psi
2 mm/min; ISO 178
115 MPa
16700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.32 GPa
336 ksi
2 mm/min; ISO 178
2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.94 J/cm
3.63 ft-lb/in
ASTM D256
1.12 J/cm

@Temperature -30.0 °C
2.10 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.40 J/cm²
11.4 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 80.0 J

@Temperature 23.0 °C
59.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Hot Ball Pressure Test <= 125 °C
<= 257 °F
IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 117 °C
243 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
140 °C
284 °F
Rate B/50; ASTM D1525
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Dmax <25
ASTM E 662
OSU total heat release (2 minute test) <55kW-min/m^2
FAR 25.853
OSU peak heat release rate (5 minute test) <55kW/m^2
FAR 25.853
Vertical Burn a (60s) passes at 2.4sec
FAR 25.853
Vertical Burn b (12s) passes at 0.5sec
FAR 25.853