SABIC Innovative Plastics Lexan® FR83 Polycarbonate Film, Flame Retardant

Category Polymer , Film , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FR83 Polycarbonate Film, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* FR83 flame-retardant film is a matt/polished, thin-gauge polycarbonate film with a UL94 VTM-0 listing to meet the stringent requirements in a wide range of electrical, electronic and transportation applications. Lexan FR83 film offers ease of thermoforming, hydroforming, embossing, die-cutting, folding, and bending and is very suitable for applications such as printed circuit board insulation, backlit aircraft in-flight panels and displays, business equipment insulation, computer rack partitions, TV and monitor insulation, PC Board insulation, and can be foil laminated for insulation and shielding.Information provided by SABIC Innovative Plastics
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Water Absorption 0.28 %
0.28 %
24 hrs; ASTM D570
Surface Tension 38 - 40 dynes/cm
38 - 40 dynes/cm
2nd surface; units: Dyne; Dyne Pens
>= 44 dynes/cm
>= 44 dynes/cm
1st surface; units: Dyne; Dyne Pens
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 60.0 MPa
8700 psi
ASTM D882
Tensile Strength, Yield 68.9 MPa
9990 psi
ASTM D882
Elongation at Break 100 - 160 %
100 - 160 %
ASTM D882
Tensile Modulus 2.20 GPa
319 ksi
ASTM D882
Gardner Impact 28.5 J

@Thickness 0.762 mm
21.0 ft-lb

@Thickness 0.0300 in
ASTM D3029
Impact Test 12.2 J
9.00 ft-lb
Puncture Resistance, Dynatup; ASTM D3763
Tear Strength 11.6 - 21.2 kN/m
66.2 - 121 pli
propogation; ASTM D1922
245 - 316 kN/m
1400 - 1800 pli
initiation; ASTM D1004
Thermal Properties Metric English Comments
CTE, linear 57.6 µm/m-°C
32.0 µin/in-°F
ASTM E831
Specific Heat Capacity 1.26 J/g-°C

@Temperature 4.00 °C
0.301 BTU/lb-°F

@Temperature 39.2 °F
ASTM E1269
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM D5470
Deflection Temperature at 1.8 MPa (264 psi) 143.3 °C
289.9 °F
TMA
Vicat Softening Point 175 °C
347 °F
ASTM 1525-00 modified
Brittleness Temperature -135 °C
-211 °F
ASTM D746
Glass Transition Temp, Tg 153 °C
307 °F
ASTM D3417/D3418
Flammability, UL94 V-0

@Thickness 0.0500 - 0.250 mm
V-0

@Thickness 0.00197 - 0.00984 in
VTM
Shrinkage 0.020 %

@Temperature 150 °C
0.020 %

@Temperature 302 °F
ASTM D1204
Optical Properties Metric English Comments
Refractive Index 1.60

@Temperature 25.0 °C
1.60

@Temperature 77.0 °F
ASTM D542A
Haze 88 %
88 %
ASTM D1003
Gloss 10 %
10 %
over Flat Black min/max @ 60º; ASTM D523-60
Yellow Index 1.1 %
1.1 %
ASTM D1925
Transmission, Visible 88 %
88 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Surface Resistivity per Square 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
ASTM D150
2.9

@Frequency 60.0 Hz
2.9

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 59.0 kV/mm

@Temperature 23.0 °C
1500 kV/in

@Temperature 73.4 °F
in oil, short time. 0.25mm; ASTM D149-97a Method A
Dissipation Factor 0.0026

@Frequency 60.0 Hz
0.0026

@Frequency 60.0 Hz
ASTM D150
0.0117

@Frequency 1.00e+6 Hz
0.0117

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 64 sec
64 sec
Tungsten; ASTM D495
Descriptive Properties Value Comments
Nominal Gauge Variation (%) 10
0.050 - 0.175mm
Surface Energy 34
1st surface; ASTM D5946-01
36
2nd surface; ASTM D5946-01