SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm).
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
foam molded; ASTM D792
1.43 g/cc
1.43 g/cc
ASTM D792
Water Absorption 0.12 %

@Time 86400 sec
 0.12 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.26 %
0.26 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 6.40 mm
 0.0020 - 0.0040 in/in

@Thickness 0.252 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 72.0 MPa

@Thickness 6.35 mm
 10400 psi

@Thickness 0.250 in
 ASTM D638
Elongation at Break 3.0 %

@Thickness 6.35 mm
 3.0 %

@Thickness 0.250 in
 ASTM D638
Tensile Modulus 6.92 GPa

@Thickness 6.40 mm
 1000 ksi

@Thickness 0.252 in
 ASTM D638
Flexural Yield Strength 127 MPa
18400 psi
6.4 mm; ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
6.4 mm; ASTM D790
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 40.0 J
29.5 ft-lb
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.6 µm/m-°C

@Temperature -40.0 - 95.0 °C
 12.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Specific Heat Capacity 1.04 J/g-°C
0.249 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.160 W/m-K
1.11 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 143 °C

@Thickness 6.40 mm
 289 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C

@Thickness 6.40 mm
 280 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 V-0

@Thickness 5.99 mm
 V-0

@Thickness 0.236 in
 UL 94
5VA

@Thickness 5.99 mm
 5VA

@Thickness 0.236 in
 UL 94
Oxygen Index 40.4 %
40.4 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+17 ohm-cm
2.40e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.10e+17 ohm
>= 1.10e+17 ohm
ASTM D257
Dielectric Constant 2.61

@Frequency 1.00e+6 Hz
 2.61

@Frequency 1.00e+6 Hz
 ASTM D150
2.7

@Frequency 100 Hz
 2.7

@Frequency 100 Hz
 ASTM D150
Dissipation Factor 0.0034

@Frequency 100 Hz
 0.0034

@Frequency 100 Hz
 ASTM D150
0.0075

@Frequency 1.00e+6 Hz
 0.0075

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20%
FOAM - Flame Class Minimum Density 0.9g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction 10%
FOAM - MECHANICAL 6.4 mm Wt Reduction 10%
FOAM - PHYSICAL 6.4mm Wt Reduction 10%
FOAM - THERMAL 6.4mm Wt Reduction 10%