SABIC Innovative Plastics Lexan® FL920 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FL920 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LEXAN FL920 is a foamable grade of LEXAN polycarbonate, containing 20% glass-fibre is designed of applications where superior flexural and tensile charasterics are required. LEXAN FL920 also offers an UL Flammability Standard 94 rating of V-0 and 5V and high heat resistance. LEXAN FL920 is the material to use for high load bearing and/or high heat applications such as in photo optical equipment, business or other large components.
Physical Properties Metric English Comments
Specific Gravity 1.00 g/cc
1.00 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 4.30 GPa
624 ksi
2 mm/min; ISO 178
Thermal Properties Metric English Comments
Thermal Conductivity 0.140 W/m-K
0.972 BTU-in/hr-ft²-°F
ISO 8302
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 V-0

@Thickness 6.00 mm
V-0

@Thickness 0.236 in
UL 94
5VA

@Thickness 6.00 mm
5VA

@Thickness 0.236 in
UL 94 by SABIC-IP
Oxygen Index 35 %
35 %
ISO 4589
Electrical Properties Metric English Comments
Dielectric Constant 2.3

@Frequency 1.00e+6 Hz
2.3

@Frequency 1.00e+6 Hz
IEC 60250
2.4

@Frequency 100 Hz
2.4

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0029

@Frequency 100 Hz
0.0029

@Frequency 100 Hz
IEC 60250
0.0081

@Frequency 1.00e+6 Hz
0.0081

@Frequency 1.00e+6 Hz
IEC 60250