SABIC Innovative Plastics Lexan® FL910 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FL910 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Various weight reductions at 0.250"" (6.35 mm) wall, 10% GR. High flexural strength and modulus, impact/heat resistant. V-0/5V at 0.250"" (6.35 mm).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | foam molded; ASTM D792 |
| 1.25 g/cc | 1.25 g/cc | ASTM D792 | |
| Water Absorption | 0.16 % @Time 86400 sec |
0.16 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 6.40 mm |
0.0040 - 0.0060 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa @Thickness 6.35 mm |
7540 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 4.8 % @Thickness 6.35 mm |
4.8 % @Thickness 0.250 in |
ASTM D638 |
| Tensile Modulus | 3.17 GPa @Thickness 6.40 mm |
460 ksi @Thickness 0.252 in |
ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 3.51 GPa | 509 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 46.0 J | 33.9 ft-lb | SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Specific Heat Capacity | 1.19 J/g-°C | 0.284 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.130 W/m-K | 0.902 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C @Thickness 6.40 mm |
271 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 2.99 mm |
V-0 @Thickness 0.118 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.40e+17 ohm-cm | 2.40e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.10e+17 ohm | >= 1.10e+17 ohm | ASTM D257 |
| Dielectric Constant | 2.4 @Frequency 1.00e+6 Hz |
2.4 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.45 @Frequency 100 Hz |
2.45 @Frequency 100 Hz |
ASTM D150 | |
| Dissipation Factor | 0.0013 @Frequency 100 Hz |
0.0013 @Frequency 100 Hz |
ASTM D150 |
| 0.0065 @Frequency 1.00e+6 Hz |
0.0065 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - Flame Class Minimum Density | 0.85g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 10% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 10% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 10% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 10% |