Material Notes:
Structural foam: 10% weight reduction at 0.250" wall. ECO-conforming. Impact modified PC with excellent low-temperature impact and UV-stability.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
foam molded; ASTM D 792
1.19 g/cc
1.19 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0090 - 0.011 cm/cm

@Thickness 6.40 mm
 0.0090 - 0.011 in/in

@Thickness 0.252 in
 SABIC Method
Melt Flow 9.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 9.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Thickness 6.35 mm
 5800 psi

@Thickness 0.250 in
 ASTM D 638
Elongation at Break 3.2 %

@Thickness 6.35 mm
 3.2 %

@Thickness 0.250 in
 ASTM D 638
Tensile Modulus 2.81 GPa

@Thickness 6.40 mm
 408 ksi

@Thickness 0.252 in
 ASTM D 638
Flexural Yield Strength 72.0 MPa

@Thickness 6.40 mm
 10400 psi

@Thickness 0.252 in
 ASTM D 790
Flexural Modulus 1.89 GPa

@Thickness 6.40 mm
 274 ksi

@Thickness 0.252 in
 ASTM D 790
Izod Impact, Unnotched 9.07 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 17.0 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D 4812
Impact Test 89.0 J

@Temperature 23.0 °C
 65.6 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
94.0 J

@Temperature -20.0 °C
 69.3 ft-lb

@Temperature -4.00 °F
 Instrumented Impact Total Energy; ASTM D 3763
94.0 J

@Temperature -40.0 °C
 69.3 ft-lb

@Temperature -40.0 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 131 °C

@Thickness 6.40 mm
 268 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C

@Thickness 6.40 mm
 248 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-0

@Thickness 2.99 mm
 V-0

@Thickness 0.118 in
 UL 94
5VA

@Thickness 6.09 mm
 5VA

@Thickness 0.240 in
 UL 94
Descriptive Properties Value Comments
FOAM - Flame Class Minimum Density, g/cm^3 1.07
-
FOAM - IMPACT 6.4 mm Wt Reduction, % 10
-
FOAM - MECHANICAL 6.4 mm Wt Reduction, % 10
-
FOAM - PHYSICAL 6.4mm Wt Reduction, % 10
-
FOAM - THERMAL 6.4mm Wt Reduction, % 10
-
UV-light, water exposure/immersion F1
UL 746C