SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
6% GF reinforced opaque polycarbonate-siloxane copolymer with good impact strength, stiffness and hydrolytic stability.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption 0.460 %
0.460 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.6 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.6 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D638
47.0 MPa
6820 psi
5 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 5 mm/min; ASTM D638
55.0 MPa
7980 psi
5 mm/min; ISO 527
Elongation at Break 15.4 %
15.4 %
5 mm/min; ISO 527
19 %
19 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.5 %
4.5 %
Type I, 5 mm/min; ASTM D638
4.6 %
4.6 %
5 mm/min; ISO 527
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
3.30 GPa
479 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 104 MPa
15100 psi
2 mm/min; ISO 178
105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.83 GPa
410 ksi
2 mm/min; ISO 178
2.85 GPa
413 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.60 J/cm
4.87 ft-lb/in
ASTM D256
1.66 J/cm

@Temperature -30.0 °C
3.11 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 39.0 J

@Temperature 23.0 °C
28.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
48.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 134 °C
273 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 146 °C
295 °F
Rate B/50; ASTM D1525
146 °C
295 °F
Rate B/50; ISO 306
148 °C
298 °F
Rate B/120; ISO 306