SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* EXL1192T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties for food contact applications. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. Lexan EXL1192T resin offers enhanced release performance, is available in transparent colors and is an excellent candidate for a broad range of applications in food handling or food preparation markets.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.090 %
0.090 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %

@Temperature 23.0 °C
0.12 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 19 g/10 min

@Load 1.20 kg,
Temperature 300 °C
19 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 89
89
ASTM D 785
Tensile Strength at Break 56.0 MPa
8120 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 117.9 %
117.9 %
Type I, 50 mm/min; ASTM D 638
119.4 %
119.4 %
50 mm/min; ISO 527
Elongation at Yield 5.4 %
5.4 %
50 mm/min; ISO 527
5.7 %
5.7 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.26 GPa
328 ksi
50 mm/min; ASTM D 638
2.34 GPa
339 ksi
1 mm/min; ISO 527
Flexural Yield Strength 89.0 MPa
12900 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.14 GPa
310 ksi
2 mm/min; ISO 178
2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 6.18 J/cm

@Temperature -30.0 °C
11.6 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
7.36 J/cm

@Temperature 23.0 °C
13.8 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
55.0 kJ/m²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.50 J/cm²

@Temperature 23.0 °C
30.9 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 74.0 J

@Temperature 23.0 °C
54.6 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.8 µm/m-°C

@Temperature -40.0 - 95.0 °C
41.6 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
74.8 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.6 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 76.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
42.4 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
76.4 µm/m-°C

@Temperature 23.0 - 80.0 °C
42.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 138 °C
280 °F
Rate A/50; ASTM D 1525
138 °C
280 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Glow Wire Test 850 °C

@Thickness 0.800 mm
1560 °F

@Thickness 0.0315 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties Metric English Comments
Haze 3.0 %

@Thickness 2.54 mm
3.0 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 82 %

@Thickness 2.54 mm
82 %

@Thickness 0.100 in
ASTM D 1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D 257
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C pass
IEC 60695-10-2