SABIC Innovative Plastics Lexan® EX2078X PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EX2078X PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* EX2078X polycarbonate resin, MVR (300°C/1.2kg) 3 cm3/10min, high viscosity, branched, extrusion, flame retardant, halogen free per DIN VDE 0472 Part 815, mold release, UV stabilized, transluscent color. Material enables a fine surface texture when extruded in sheet, pipe and profiles.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Melt Index of Compound 3.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
3.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
6.0 g/10 min

@Load 2.16 kg,
Temperature 300 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Yield 7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*3; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
286 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 128 °C
262 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 140 °C
284 °F
Rate B/120; ISO 306
148 °C
298 °F
Rate B/50; ISO 306
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL 94
Glow Wire Test 960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
IEC 60695-2-12