SABIC Innovative Plastics Lexan® EM3110 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® EM3110 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.16 % @Time 86400 sec |
0.16 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 2.13 J/cm @Temperature -30.0 °C |
3.99 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 5.87 J/cm @Temperature -20.0 °C |
11.0 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| 2.13 J/cm @Thickness 6.40 mm |
3.99 ft-lb/in @Thickness 0.252 in |
ASTM D256 | |
| Dart Drop, Total Energy | 56.0 J | 41.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
Users viewing this material also viewed the following:
- Polymer Resources PC-UV1-D-[color]-1 Polycarbonate, UV-stabilized, Low Flow with Mold Release
- Huntsman IROGRAN® A 95 P 5003 TPU-Polyether
- LG Chemical Lupox® PBT-GP-2156F 15% GFR Flame Retardant PBT
- Styron EMERGEâ„¢ 7700 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- Goodfellow Tungsten 75/Rhenium 25 Alloy
- Eagle Brass 511 Phosphor Bronzes 4%, 1/4 Hard
- ChevronTexaco ParaMount™ 6005 Paraffinic Process Oil
- ExxonMobil 312 Mobilgard 12 Series
- Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- DuPont Performance Polymers Zytel® 77G43L BK031 Nylon 612 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved