SABIC Innovative Plastics Lexan® EM1210 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® EM1210 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.16 % @Time 86400 sec |
0.16 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 1.20 kg, Temperature 300 °C |
13 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 7.74 J/cm | 14.5 ft-lb/in | ASTM D256 |
| 6.94 J/cm @Temperature -30.0 °C |
13.0 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.94 J/cm @Thickness 6.40 mm |
13.0 ft-lb/in @Thickness 0.252 in |
ASTM D256 | |
| Dart Drop, Total Energy | 61.0 J | 45.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 65.0 J @Temperature -30.0 °C |
47.9 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® HPV PEEK High Pressure Velocity Polyetherether Ketone (ASTM Product Data Sheet)
- Lord Adhesives 648 Low Odor, Low Flammability, Non Sag, Metal Use Acrylic Adhesive
- Isoflon PEI Polyetherimide
- Techmer ES HiFill FR® PA4/6 GF30 FR HS X 30% Glass Filled (Dry)
- Shuman FR310 Utility Black PC/ABS Alloy, Flame Retardant
- Trelleborg R395 Natural Rubber Polyisoprene
- Chesterton 235 SSC Liquid alkaline degreaser
- Chicago Extruded Metals BioBrass® UNS C27000 Copper-Zinc Alloy
- Aaron Industries AAROPRENE® ATPR 1000 50A Elastomeric Compound
- 3A Composites Core Materials AIREX® PXw.385 Fiber-Reinforced Structural Foam Panel
Copyright © lookpolymers.com All Rights Reserved