SABIC Innovative Plastics Lexan® DMX3415M PC Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® DMX3415M PC Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* DMX3415M is a co-polycarbonate resin with improved scratch and abrasion resistance compared to standard polycarbonate. Lexan* DMX3415M is available in transparent colors.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.27 %
0.27 %
ISO 62
Melt Flow 17.9 g/10 min

@Load 1.20 kg,
Temperature 300 °C
17.9 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
Type I, 50 mm/min; ASTM D638
80.0 MPa
11600 psi
50 mm/min; ISO 527
Elongation at Break 27 %
27 %
50 mm/min; ISO 527
36 %
36 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
2.90 GPa
421 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 108 MPa
15700 psi
2 mm/min; ISO 178
120 MPa
17400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.45 GPa
355 ksi
2 mm/min; ISO 178
2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.300 J/cm
0.562 ft-lb/in
ASTM D256
0.300 J/cm

@Temperature -30.0 °C
0.562 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*3; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
45.0 kJ/m²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
4.70 J/cm²

@Temperature -30.0 °C
22.4 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ASTM E 831
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
129 °C

@Thickness 3.20 mm
264 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 114 °C
237 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
115 °C

@Thickness 3.20 mm
239 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 134 °C
273 °F
Rate B/50; ISO 306
136 °C
277 °F
Rate B/120; ISO 306
139 °C
282 °F
Rate B/50; ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.584
1.584
ASTM D542
1.584
1.584
ISO 489
Haze <= 1.0 %

@Thickness 2.54 mm
<= 1.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003
Descriptive Properties Value Comments
Pencil Hardness test, 1kgf H
ASTM D3363